Non-asbestos composite gasket sheet
Other name: Non-asbestos composite Gasket Sheet, Non-asbestos composite sheet, Reinforced non-asbestos sheet, Non-asbestos composite beater sheet, Non-asbestos beater sheet.
Manufactured from non-asbestos beater sheet(100% not contain asbestos) with mechanically clinched to 0.18 ~ 0.25mm thick carbon steel tanged (perforated) metal sheet - 08F tinplate insert. It is best gasket material for motorcycle and automobile cylinder head gasket.
This series include:
- Reinforced non-asbestos Composite Sheet.
- Reinforced non-asbestos Composite Sheet with Both Size Coating Graphite.
- Two or more Layers Steel Inserted Reinforced Non-Asbestos Sheet.
- Reinforced Non-Asbestos Sheet With Both Size Coating Silicon Resin (anti stick).
Available Size:
Thickness: 1.0mm ~ 3.0mm.
400mm x 1000mm, 500mm x 1000mm, 500mm x 1200mm, 500mm x 1500mm, 510mm x 1016mm, 510mm x 1530mm, 1000mm x 1000mm, 1000mm x 1500mm.
Color: Gray, Black.
The other size is optional or according to the requirements of customers.
Product Date Sheet
| Item |
Standard data |
| Density g/cm³ |
1.3～1.5 |
| working temperature ℃ |
150～300 |
| Compressibility % |
10±5 |
| Recovery ≥ % |
40 |
| Sealing performance |
<0.5cm3/min |
| causticity |
Cusp no rusty |
| Tensile strength MPa ≥ |
12.7 |
| Compressive Strength MPa ≥ |
80.0 |
| Carbon content≥ % |
98 |
| Ash content ＜% |
1 |
| With the temperature of 150±2℃, Soaking 20# fluid oil for 5 hours, MPa≥ |
oil absorption %≤ |
25 |
| Thickness-increasing %≤ |
0～10 |
| Stripping performance |
No stripe |
| With the temperature of 15 to 30℃, Soaking 75# kerosene for 5 hours, MPa≥ |
oil absorption %≤ |
15 |
| Thickness-increasing %≤ |
0～15 |
| Stripping performance |
No stripe |
| With the temperature of 100℃, Soaking distilled water for 5 hours, MPa≥ |
water absorption %≤ |
15 |
| Thickness-increasing %≤ |
0～15 |
| Stripping performance |
No strip
|